| Products Name |
: |
Permanent Red FGR - ID |
|
| Code No. |
: |
4203166 |
|
| Chemical Class |
: |
Monoazo Red - Napthol AS range |
|
| Colour Index Name |
: |
Pigment Red 112 |
|
| Colour Index No. |
: |
12370 |
|
| Basic Pigment C A S No. |
: |
6535-46-2 |
|
|
|
|
|
|
|
| |
|
|
|
|
| Permanent Red FGR - ID is a medium red shade pigment with
excellent light and weather fastness properties and high colour strength. |
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity at 20°c |
: |
1.410 |
|
| Sieve Residue |
: |
0.1 % max |
|
| Moisture Content |
: |
1.0 % max |
|
| pH of Water Extract |
: |
6.0 to 8.0 |
|
| Specific Conductivity |
: |
< 0.5 ms cm-1 |
|
| |
|
|
|
| SPECTROPHOTOMETRY / TYPICAL
VALUES |
| D65 / 100 / Spec.Inclusive
/ small area view / 80 diffuse |
| CIELAB |
L |
C |
h |
| Full shade |
40.95 |
52.83 |
29.73 |
| Reduction |
55.21 |
45.73 |
10.39 |
| L = Lightness/Darkness
C = Chroma h = hue angle |
|
|
|
|
|
|
|
|
|
| Characteristics |
Printing Inks |
Paints |
Plastics |
New Systems |
| |
1/1
Depth |
1/25
Depth |
1/1
Depth |
1/25
Depth |
1/1
Depth |
1/25
Depth |
1/1
Depth |
1/25
Depth |
| Light Fastness (1-8 Scale) |
6-7
|
6
|
7-8
|
6
|
-
|
-
|
7-8
|
6
|
| Weather Fastness (1-5 scale ) |
-
|
-
|
4-5
|
3
|
-
|
-
|
-
|
-
|
| Heat Stability celcius |
180oC-10min
|
180oC
|
-
|
180oC
|
| Solvent Fastness (1-5 scale ) - General |
3-4
|
-
|
-
|
-
|
| Soap Fastness (1-5 scale ) Print |
3-4
|
-
|
-
|
3-4
|
| Fastness to Bleed - PVC |
-
|
-
|
-
|
-
|
| Over Spray Fasteness (1- 5 scale ) - Paint |
-
|
3
|
-
|
-
|
| Key : (1-8 scale ) 1 - Poor ; 8 - Excellent
(1-5 scale) 1- Poor ; 5 - Excellent
d- darkens |
|
|
|
|
|
|
|
| Printing Inks |
|
Paints |
|
Plastics |
New System |
|
| Letterpress Inks |
|
Deco airdrying paints |
|
|
Textile emulsion |
|
| Offset Inks |
|
Deco emulsion paints |
|
|
|
|
| Flexo Inks |
|
Industrial finishes |
|
|
|
|
| Metal Deco Inks |
|
Stoving paints |
|
|
|
|
| Silk Screen Inks |
|
Dry colours |
|
|
|
|
| |
|
Powder coatings |
|
|
|
|
| |
|
Automotive repair finishes |
|
|
|
|
| |
|
|
|
|
|
|
| |
|
|
|
|
|
|
| |
|
|